Analysis of the shortcomings of several major parts after heat treatment of nsk imported bearings

Source: Bearing network time: 2018-01-07

/*250*250 was created on 2017/12/25*/ var cpro_id = 'u3171089';

1. The outer decarburization bearing parts are in the heat treatment process; if it is heated in an oxidizing medium; the surface will have an oxidation effect to reduce the mass fraction of the surface carbon of the part; the outer surface decarburization is formed. The depth of the outer decarburization layer exceeds the final processing. The amount of waste will make the part invalid. The determination of the depth of the decarburization layer can be determined by the metallographic method and the microhardness method in the metallographic examination. The measurement method of the surface microhardness dispersion curve is the standard; the ruling criterion can be made.
2. Heat treatment of deformed bearing parts during heat treatment; there are thermal stresses and arrangement stresses; such internal stresses can be superimposed or partially offset; they are complex and variable; because they can follow heating temperature, heating rate, cooling method, cooling rate, parts The shape and the size change, so the heat treatment deformation is inevitable. Knowing and grasping the changing rules can make the deformation of the bearing parts (such as the ellipse of the ferrule, the scale increase, etc.) on a controllable scale; Of course, the mechanical bump during the heat treatment will also deform the part; but this deformation can be reduced and prevented by the improved operation.
3. Quenching cracked bearing parts are called quenching cracks due to internal stress during quenching and cooling. The causes of such cracks are: because the quenching heating temperature is too high or the cooling is too fast; the thermal stress and the metal mass volume change the arrangement stress It is greater than the fracture strength of the steel, the original defects of the work appearance (such as fine cracks or scratches on the surface) or the internal defects of the steel (such as slag inclusions, severe non-metallic inclusions, white spots, shrinkage holes, etc.) during quenching Constitutive stress gathering, severe surface decarburization and carbide segregation, lack of tempering after quenching of parts or tempering in time, the cold pressing stress of the previous process is too large, casting folding, deep turning tool marks, oil groove sharp edge The reason for the quenching crack may be one or more of the above factors; the existence of internal stress is the main reason for the quenching crack. The quenching crack is deep and slender; the fracture is straight; the fracture has no oxidation color. On the bearing ring, there are often longitudinal straight cracks or ring cracks. The shape of the bearing steel ball is S-shaped, T-shaped or ring-shaped. The quenching crack is arranged on both sides of the crack. Carbon appearance; significantly different from the casting crack and crack data.

Recommend to friends comments close window

Bearing related knowledge

What are the classifications of sliding bearings?
The minimum load calculation formula of skf double row cylindrical roller bearing and the smoothness of the main bearing of cement mill
High Temperature Adaptability of NTN Bearings Talk about the High Temperature Adaptability of FAG Advanced Angle Touch Ball Bearings

This article links to http://
Please indicate China Bearing Network http://

Previous:KOYO Spherical Roller Bearings Next: Chongqing Yangtze River Bearing: Analysis of Wheel Bearing Skills

Electric Actuator

Electric Actuator,Mini Electric Valve,Electric Actuator Valve,Electric Rotary Actuator

WENZHOU FOREVER CLASSIC TECHNOLOGY CO.,LTD , https://www.fosicvalve.com